品牌:瑞典伊萨焊材
3.2:450
4.0:450
5.0:450
起订:20kg
供应:18000kg
发货:3天内
OK13Mn可熔敷能够通过冲击应力和压应力冷作硬化的奥氏体锰钢。焊条主要用于破碎机颚板和锤等锰钢组件的堆焊和修造。层间温度应尽可能低。
| 分类: | E Fe9, EN 14700 |
| Alloy Type: | Austenitic Mn steel |
| Coating Type: | Lime Basic |
| Welding Current: | AC, DC+ |
焊缝金属分析
夏比V型缺口冲击性能
| ISO As welded | |
| Impact Value | Testing Temperature |
| 70 J | 20 °C |
| 45 J | -20 °C |
| 35 J | -40 °C |
| 25 J | -60 °C |
Typical Tensile Properties
| ISO As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 20 % | 780 MPa | 480 MPa |
熔敷数据
| Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
| 95 sec | 0.60 kg | 36 | 95-135 A | 1.1 kg/h | 23 V | 3.2 x 450 mm |
| 109 sec | 0.60 kg | 24 | 130-180 A | 1.4 kg/h | 23 V | 4.0 x 450 mm |
| 132 sec | 0.60 kg | 15 | 170-230 A | 1.8 kg/h | 25 V | 5.0 x 450 mm |